The electrolytic Zinc process consists in the deposition of metallic Zn by the passage of current within a specific electrolyte. In this way, bright deposits of Zn are obtained on metal parts of different materials such as steel, zamak, brass, etc.
The purpose of Zn coatings is the corrosion protection of the material that is coated. This is achieved through two mechanisms:
1.- Physical barrier isolating the coated material against the oxidizing medium.
2.- Cathodic protection, with which the deposited Zn layer acts as a sacrificial metal against the coated material, protecting it. This property is one of the main advantages of Zn coatings and their alloys over other types of coatings.
Among the advantages of the electrodeposited Zn coating, compared to other coatings, the low thickness necessary to obtain good corrosion protection (usually working in the range of 8 to 20 microns) stands out, the excellent adhesion with the base metal to Coating, the protective capacity against sacrificial corrosion and good reactivity for the application of passivation layers and subsequent seals.
The treatments of electrolytic Zn are applied both in static, by means of racks where the pieces are covered unitarily, or in drums, where the treatment is in mass. For each piece the appropriate treatment method should be applied depending on its size, geometry, etc.
Passivations that are conversion coatings can be applied to the Zn tank through the use of CrVI salts to protect the tank against corrosion. These passivations are those that give the colour to the finish, being able to be bluish, iridescent yellow or black.
With the application of TOP COAT of high layer in the final phase of the process, a more homogeneous final appearance is achieved, corrosion resistance is considerably increased both to white corrosion (coating corrosion), and to red corrosion (steel corrosion) and the friction coefficient is parameterized according to the requested specification.